Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes

Autores
Canosa, Guadalupe; Alfieri, Paula; Giúdice, Carlos Alberto
Año de publicación
2013
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The wood, very heterogeneous and complex material, changes its volume by water absorption or desorption causing swelling or shrinkage and also it can be degraded both by action of microorganisms and fire; the above-mentioned is a great inconvenient for most commercial uses. In this research, wood specimens of Pinus radiata were previously pretreated in a Soxhlet extractor for 2 hours with a solution of sodium hydroxide (activation of the cellulose) and then impregnated with alkylalkoxysilanes hydrolyzed and condensed "in situ" by the sol-gel process. Silanes selected were triethoxysilane, methyltriethoxysilane, n-propyltriethoxysilane, n-buthyltriethoxysilane and n-octhyltriethoxysilane. Impregnation process was carried out under controlled operating conditions to achieve similar weight gains of the chemical modifier. The pH was adjusted to alkaline value for controlling kinetic of hydrolysis and condensation reactions. Results indicated that dimensional stability increased with the increase of the length of the hydrocarbon chain of the alkoxydes, which would be based essentially on their enhanced hydrophobicity but without discarding the partial occupation of the pores by polymerized siloxanes and the interaction of alkoxides with cell wall components. In addition, wood specimens impregnated with mentioned alkylalkoxysilanes also showed an excellent fire performance and decay resistance.
Fil: Alfieri, Paula V. CIDEPINT (Centro de Investigación y Desarrollo en Tecnología de Pinturas); Argentina
Fil: Giúdice, Carlos Alberto. UTN (Universidad Tecnológica Nacional); Argentina. CIDEPINT (Centro de Investigación y Desarrollo en Tecnología de Pinturas); Argentina
Fil: Canosa, Guadalupe. UTN (Universidad Tecnológica Nacional); Argentina
Peer Reviewed
Materia
Wood
Impregnation
Alkylalkoxysilane
Dimensional stability
Fire performance
Decay resistance
Nivel de accesibilidad
acceso abierto
Condiciones de uso
2017-10-25T18:52:18Z
Repositorio
Repositorio Institucional Abierto (UTN)
Institución
Universidad Tecnológica Nacional
OAI Identificador
oai:ria.utn.edu.ar:20.500.12272/2197
Acceder
id RIAUTN_3f1a7f74bf66b63a6d91c59ce3385605
oai_identifier_str oai:ria.utn.edu.ar:20.500.12272/2197
network_acronym_str RIAUTN
repository_id_str a
network_name_str Repositorio Institucional Abierto (UTN)
spelling Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanesCanosa, GuadalupeAlfieri, PaulaGiúdice, Carlos AlbertoWoodImpregnationAlkylalkoxysilaneDimensional stabilityFire performanceDecay resistanceThe wood, very heterogeneous and complex material, changes its volume by water absorption or desorption causing swelling or shrinkage and also it can be degraded both by action of microorganisms and fire; the above-mentioned is a great inconvenient for most commercial uses. In this research, wood specimens of Pinus radiata were previously pretreated in a Soxhlet extractor for 2 hours with a solution of sodium hydroxide (activation of the cellulose) and then impregnated with alkylalkoxysilanes hydrolyzed and condensed "in situ" by the sol-gel process. Silanes selected were triethoxysilane, methyltriethoxysilane, n-propyltriethoxysilane, n-buthyltriethoxysilane and n-octhyltriethoxysilane. Impregnation process was carried out under controlled operating conditions to achieve similar weight gains of the chemical modifier. The pH was adjusted to alkaline value for controlling kinetic of hydrolysis and condensation reactions. Results indicated that dimensional stability increased with the increase of the length of the hydrocarbon chain of the alkoxydes, which would be based essentially on their enhanced hydrophobicity but without discarding the partial occupation of the pores by polymerized siloxanes and the interaction of alkoxides with cell wall components. In addition, wood specimens impregnated with mentioned alkylalkoxysilanes also showed an excellent fire performance and decay resistance.Fil: Alfieri, Paula V. CIDEPINT (Centro de Investigación y Desarrollo en Tecnología de Pinturas); ArgentinaFil: Giúdice, Carlos Alberto. UTN (Universidad Tecnológica Nacional); Argentina. CIDEPINT (Centro de Investigación y Desarrollo en Tecnología de Pinturas); ArgentinaFil: Canosa, Guadalupe. UTN (Universidad Tecnológica Nacional); ArgentinaPeer Reviewed2017-10-25T18:52:18Z2017-10-25T18:52:18Z2013-11-20info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/20.500.12272/2197enginfo:eu-repo/semantics/openAccess2017-10-25T18:52:18ZAtribución (Attribution): En cualquier explotación de la obra autorizada por la licencia será necesario reconocer la autoría (obligatoria en todos los casos). No comercial (Non Commercial): La explotación de la obra queda limitada a usos no comerciales. Sin obras derivadas (No Derivate Works): La autorización para explotar la obra no incluye la posibilidad de crear una obra derivada (traducciones, adaptaciones, etc.). Compartir igual (Share Alike): La explotación autorizada incluye la creación de obras derivadas siempre que se mantenga la misma licencia al ser divulgadas.reponame:Repositorio Institucional Abierto (UTN)instname:Universidad Tecnológica Nacional2026-09-24T12:45:09Zoai:ria.utn.edu.ar:20.500.12272/2197instacron:UTNInstitucionalhttp://ria.utn.edu.ar/Universidad públicaNo correspondehttp://ria.utn.edu.ar/oaigestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:a2026-09-24 12:45:09.959Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacionalfalse
dc.title.none.fl_str_mv Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
title Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
spellingShingle Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
Canosa, Guadalupe
Wood
Impregnation
Alkylalkoxysilane
Dimensional stability
Fire performance
Decay resistance
title_short Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
title_full Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
title_fullStr Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
title_full_unstemmed Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
title_sort Dimensional stability, fire performance and decay resistance in wood impregnated with alkylalkoxysilanes
dc.creator.none.fl_str_mv Canosa, Guadalupe
Alfieri, Paula
Giúdice, Carlos Alberto
author Canosa, Guadalupe
author_facet Canosa, Guadalupe
Alfieri, Paula
Giúdice, Carlos Alberto
author_role author
author2 Alfieri, Paula
Giúdice, Carlos Alberto
author2_role author
author
dc.subject.none.fl_str_mv Wood
Impregnation
Alkylalkoxysilane
Dimensional stability
Fire performance
Decay resistance
topic Wood
Impregnation
Alkylalkoxysilane
Dimensional stability
Fire performance
Decay resistance
dc.description.none.fl_txt_mv The wood, very heterogeneous and complex material, changes its volume by water absorption or desorption causing swelling or shrinkage and also it can be degraded both by action of microorganisms and fire; the above-mentioned is a great inconvenient for most commercial uses. In this research, wood specimens of Pinus radiata were previously pretreated in a Soxhlet extractor for 2 hours with a solution of sodium hydroxide (activation of the cellulose) and then impregnated with alkylalkoxysilanes hydrolyzed and condensed "in situ" by the sol-gel process. Silanes selected were triethoxysilane, methyltriethoxysilane, n-propyltriethoxysilane, n-buthyltriethoxysilane and n-octhyltriethoxysilane. Impregnation process was carried out under controlled operating conditions to achieve similar weight gains of the chemical modifier. The pH was adjusted to alkaline value for controlling kinetic of hydrolysis and condensation reactions. Results indicated that dimensional stability increased with the increase of the length of the hydrocarbon chain of the alkoxydes, which would be based essentially on their enhanced hydrophobicity but without discarding the partial occupation of the pores by polymerized siloxanes and the interaction of alkoxides with cell wall components. In addition, wood specimens impregnated with mentioned alkylalkoxysilanes also showed an excellent fire performance and decay resistance.
Fil: Alfieri, Paula V. CIDEPINT (Centro de Investigación y Desarrollo en Tecnología de Pinturas); Argentina
Fil: Giúdice, Carlos Alberto. UTN (Universidad Tecnológica Nacional); Argentina. CIDEPINT (Centro de Investigación y Desarrollo en Tecnología de Pinturas); Argentina
Fil: Canosa, Guadalupe. UTN (Universidad Tecnológica Nacional); Argentina
Peer Reviewed
description The wood, very heterogeneous and complex material, changes its volume by water absorption or desorption causing swelling or shrinkage and also it can be degraded both by action of microorganisms and fire; the above-mentioned is a great inconvenient for most commercial uses. In this research, wood specimens of Pinus radiata were previously pretreated in a Soxhlet extractor for 2 hours with a solution of sodium hydroxide (activation of the cellulose) and then impregnated with alkylalkoxysilanes hydrolyzed and condensed "in situ" by the sol-gel process. Silanes selected were triethoxysilane, methyltriethoxysilane, n-propyltriethoxysilane, n-buthyltriethoxysilane and n-octhyltriethoxysilane. Impregnation process was carried out under controlled operating conditions to achieve similar weight gains of the chemical modifier. The pH was adjusted to alkaline value for controlling kinetic of hydrolysis and condensation reactions. Results indicated that dimensional stability increased with the increase of the length of the hydrocarbon chain of the alkoxydes, which would be based essentially on their enhanced hydrophobicity but without discarding the partial occupation of the pores by polymerized siloxanes and the interaction of alkoxides with cell wall components. In addition, wood specimens impregnated with mentioned alkylalkoxysilanes also showed an excellent fire performance and decay resistance.
publishDate 2013
dc.date.none.fl_str_mv 2013-11-20
2017-10-25T18:52:18Z
2017-10-25T18:52:18Z
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/20.500.12272/2197
url http://hdl.handle.net/20.500.12272/2197
dc.language.none.fl_str_mv eng
language eng
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
2017-10-25T18:52:18Z
Atribución (Attribution): En cualquier explotación de la obra autorizada por la licencia será necesario reconocer la autoría (obligatoria en todos los casos). No comercial (Non Commercial): La explotación de la obra queda limitada a usos no comerciales. Sin obras derivadas (No Derivate Works): La autorización para explotar la obra no incluye la posibilidad de crear una obra derivada (traducciones, adaptaciones, etc.). Compartir igual (Share Alike): La explotación autorizada incluye la creación de obras derivadas siempre que se mantenga la misma licencia al ser divulgadas.
eu_rights_str_mv openAccess
rights_invalid_str_mv 2017-10-25T18:52:18Z
Atribución (Attribution): En cualquier explotación de la obra autorizada por la licencia será necesario reconocer la autoría (obligatoria en todos los casos). No comercial (Non Commercial): La explotación de la obra queda limitada a usos no comerciales. Sin obras derivadas (No Derivate Works): La autorización para explotar la obra no incluye la posibilidad de crear una obra derivada (traducciones, adaptaciones, etc.). Compartir igual (Share Alike): La explotación autorizada incluye la creación de obras derivadas siempre que se mantenga la misma licencia al ser divulgadas.
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.source.none.fl_str_mv reponame:Repositorio Institucional Abierto (UTN)
instname:Universidad Tecnológica Nacional
reponame_str Repositorio Institucional Abierto (UTN)
collection Repositorio Institucional Abierto (UTN)
instname_str Universidad Tecnológica Nacional
repository.name.fl_str_mv Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacional
repository.mail.fl_str_mv gestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.ar
_version_ 1877230894960345088
score 12.733355

Publicaciones similares