Thermal stability of DLC coating deposited on precipitation hardening stainless steels

Autores
Dalibón Bähler, Eugenia Laura; Ghafoor, Naureen; Rogström, Lina; Trava-Airoldi, Vladimir Jesús; Odén, Magnus; Brühl, Sonia Patricia
Año de publicación
2015
Idioma
inglés
Tipo de recurso
documento de conferencia
Estado
versión aceptada
Descripción
Relationship between nanohardness and annealing temperature of DLC coating on duplex (previously nitrided) and only coated PH steel samples.
The DLC (Diamond Like Carbon) coatings are characterized by good mechanical properties, low friction coefficient and chemical inertness. However, these coatings have problems at high temperature (400 °C) owing to the graphitization which leads to an increase in sp2 and decrease in sp3 bonding structure. In this work, the thermal stability of DLC coatings deposited by PACVD (Plasma-assisted chemical vapor deposition) on nitrided precipitation hardening stainless steel (duplex sample) and without nitriding (coated sample) was studied. The annealing treatments were carried out at 200 °C , 300 °C, 400 °C , 500 °C , 600 °C, 700 °C for 1 hour on coated and duplex samples in vacuum, according to some reports found in the literature. The coatings were characterized by EDS and Raman and hardness was assessed with nanoindentation. The microstructure of the nitrided layer and the coatings was analyzed by OM and SEM. The coatings had about 12 % hydrogen content and the film thickness was about 3 m. The mean hardness of the duplex sample was 16 GPa without annealing, but it did not decrease and remained approximately constant until 600 °C. However, in the coated sample, the hardness decreased at 300 °C, probably because the sp2 bonds percentage increased in the coating. Moreover, at 600 °C, it was not possible to obtain a value for the nanohardness because the dispersion resulted very large. This could be due to coating detachment in several regions, probably caused by film transformation (graphitization) in these zones. It is possible that in the duplex sample, the nitriding process as previous treatment to the coating deposition improved the thermal behavior of the system. Future analysis will be performed in order to identify the compounds that were formed in the interface of the duplex sample.
Los recubrimientos DLC (Diamond Like Carbon) se caracterizan por sus buenas propiedades mecánicas, bajo coeficiente de fricción e inercia química. Sin embargo, estos recubrimientos tienen problemas a alta temperatura (400 °C) debido a que se produce la grafitización que conduce a un aumento de uniones sp2 y a una disminución de las uniones sp3. En este trabajo, se estudió la estabilidad térmica de los recubrimientos DLC depositados por PACVD (Plasma-assisted chemical vapor deposition) sobre acero inoxidable endurecible por precipitación nitrurado (muestra duplex) y sin nitrurar (muestra recubierta). Los tratamientos de recocidos se llevaron a cabo a 200 °C, 300 °C, 400 °C, 500 °C, 600 °C y 700 °C durante una hora en vacío en la muestra duplex y recubierta, de acuerdo a lo reportado en la literatura. Los recubrimientos fueron caracterizados por EDS y Raman y la dureza fue medida con nanoindentación. La microestructura de la capa nitrurada y del recubrimiento fue analizada por OM y SEM. El recubrimiento tuvo un contenido de hidrógeno de aproximadamente el 12 % y su espesor fue de aproximadamente 3 m. El valor de dureza promedio en la muestra duplex fue de 16 GPa antes del recocido y permaneció aproximadamente constante hasta 600 °C. Sin embargo, en la muestra recubierta, la dureza disminuyó a los 300 °C probablemente porque el porcentaje de uniones sp2 aumentó en el recubrimiento. Además a 600 °C no fue posible obtener un valor para la nanodureza porque hubo una gran dispersión en los valores. Esto podría deberse a que el recubrimiento se desprendió en algunas regiones probablemente a causa de su grafitización en esas zonas. Es posible que en la muestra duplex, el proceso de nitruración previo al tratamiento de deposición del recubrimiento mejoró el comportamiento térmico del sistema. En el futuro, se realizarán análisis para identificar los compuestos que se forman en la interfase de la muestra duplex.
Fil: Dalibón Bähler, Eugenia Laura. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.
Fil: Ghafoor, Naureen. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.
Fil: Rogström, Lina. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.
Fil: Trava-Airoldi, Vladimir Jesús. Instituto Nacional de Pesquisas Espaciáis; Brazil.
Fil: Odén, Magnus. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.
Fil: Brühl, Sonia Patricia. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.
Peer Reviewed
Materia
DLC coating
Duplex treatment
Thermal stability
Stainless steel
Recubrimientos DLC
Tratamientos duplex
Estabilidad térmica
Aceros inoxidables
Nivel de accesibilidad
acceso abierto
Condiciones de uso
2016-06-16T21:52:47Z
Repositorio
Repositorio Institucional Abierto (UTN)
Institución
Universidad Tecnológica Nacional
OAI Identificador
oai:ria.utn.edu.ar:20.500.12272/815
Acceder
id RIAUTN_c71c9e106c74b6e31d7992dbdda4816a
oai_identifier_str oai:ria.utn.edu.ar:20.500.12272/815
network_acronym_str RIAUTN
repository_id_str a
network_name_str Repositorio Institucional Abierto (UTN)
spelling Thermal stability of DLC coating deposited on precipitation hardening stainless steelsTopic : 21. Thin films and surface treatments thermal stability of DLC coating deposited on precipitation hardening stainless steelsDalibón Bähler, Eugenia LauraGhafoor, NaureenRogström, LinaTrava-Airoldi, Vladimir JesúsOdén, MagnusBrühl, Sonia PatriciaDLC coatingDuplex treatmentThermal stabilityStainless steelRecubrimientos DLCTratamientos duplexEstabilidad térmicaAceros inoxidablesRelationship between nanohardness and annealing temperature of DLC coating on duplex (previously nitrided) and only coated PH steel samples.The DLC (Diamond Like Carbon) coatings are characterized by good mechanical properties, low friction coefficient and chemical inertness. However, these coatings have problems at high temperature (400 °C) owing to the graphitization which leads to an increase in sp2 and decrease in sp3 bonding structure. In this work, the thermal stability of DLC coatings deposited by PACVD (Plasma-assisted chemical vapor deposition) on nitrided precipitation hardening stainless steel (duplex sample) and without nitriding (coated sample) was studied. The annealing treatments were carried out at 200 °C , 300 °C, 400 °C , 500 °C , 600 °C, 700 °C for 1 hour on coated and duplex samples in vacuum, according to some reports found in the literature. The coatings were characterized by EDS and Raman and hardness was assessed with nanoindentation. The microstructure of the nitrided layer and the coatings was analyzed by OM and SEM. The coatings had about 12 % hydrogen content and the film thickness was about 3 m. The mean hardness of the duplex sample was 16 GPa without annealing, but it did not decrease and remained approximately constant until 600 °C. However, in the coated sample, the hardness decreased at 300 °C, probably because the sp2 bonds percentage increased in the coating. Moreover, at 600 °C, it was not possible to obtain a value for the nanohardness because the dispersion resulted very large. This could be due to coating detachment in several regions, probably caused by film transformation (graphitization) in these zones. It is possible that in the duplex sample, the nitriding process as previous treatment to the coating deposition improved the thermal behavior of the system. Future analysis will be performed in order to identify the compounds that were formed in the interface of the duplex sample.Los recubrimientos DLC (Diamond Like Carbon) se caracterizan por sus buenas propiedades mecánicas, bajo coeficiente de fricción e inercia química. Sin embargo, estos recubrimientos tienen problemas a alta temperatura (400 °C) debido a que se produce la grafitización que conduce a un aumento de uniones sp2 y a una disminución de las uniones sp3. En este trabajo, se estudió la estabilidad térmica de los recubrimientos DLC depositados por PACVD (Plasma-assisted chemical vapor deposition) sobre acero inoxidable endurecible por precipitación nitrurado (muestra duplex) y sin nitrurar (muestra recubierta). Los tratamientos de recocidos se llevaron a cabo a 200 °C, 300 °C, 400 °C, 500 °C, 600 °C y 700 °C durante una hora en vacío en la muestra duplex y recubierta, de acuerdo a lo reportado en la literatura. Los recubrimientos fueron caracterizados por EDS y Raman y la dureza fue medida con nanoindentación. La microestructura de la capa nitrurada y del recubrimiento fue analizada por OM y SEM. El recubrimiento tuvo un contenido de hidrógeno de aproximadamente el 12 % y su espesor fue de aproximadamente 3 m. El valor de dureza promedio en la muestra duplex fue de 16 GPa antes del recocido y permaneció aproximadamente constante hasta 600 °C. Sin embargo, en la muestra recubierta, la dureza disminuyó a los 300 °C probablemente porque el porcentaje de uniones sp2 aumentó en el recubrimiento. Además a 600 °C no fue posible obtener un valor para la nanodureza porque hubo una gran dispersión en los valores. Esto podría deberse a que el recubrimiento se desprendió en algunas regiones probablemente a causa de su grafitización en esas zonas. Es posible que en la muestra duplex, el proceso de nitruración previo al tratamiento de deposición del recubrimiento mejoró el comportamiento térmico del sistema. En el futuro, se realizarán análisis para identificar los compuestos que se forman en la interfase de la muestra duplex.Fil: Dalibón Bähler, Eugenia Laura. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.Fil: Ghafoor, Naureen. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.Fil: Rogström, Lina. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.Fil: Trava-Airoldi, Vladimir Jesús. Instituto Nacional de Pesquisas Espaciáis; Brazil.Fil: Odén, Magnus. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.Fil: Brühl, Sonia Patricia. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.Peer Reviewed2016-06-16T21:52:47Z2016-06-16T21:52:47Z2015-11-17info:eu-repo/semantics/conferenceObjectinfo:eu-repo/semantics/acceptedVersiondocunento de conferenciahttp://purl.org/coar/resource_type/c_5794info:ar-repo/semantics/documentoDeConferenciaapplication/pdfapplication/pdf15º Congreso Internacional de Metalurgia y Materiales CONAMET/SAM. Chile (2015)http://hdl.handle.net/20.500.12272/815engH. Li, T. Xu, et al. "Annealing effect on the structure, mechanical and tribological properties of hydrogenated diamond-like carbon films" Thin Solid Films 2006 515 (4) 2153–2160Y.S. Zou, Y.F. Wu, et al. "Mechanical properties and thermal stability of nitrogen incorporated diamond-like carbon films", Vacuum 2009 83 (11) 1406–1410.Zhang, X.L. Bui, et al, "Thermal stability and oxidation properties of magnetron sputtered diamond-like carbon and its nanocomposite coatings". Diam. Relat. Mater. 2006 15 (4-8) 972–976.H.W. Choi, D.M. Gage, et al. "Effects of thermal annealing and Si incorporation on bonding structure and fracture properties of diamond-like carbon films". Diam. Relat. Mater. 2009 18 (4) 615–619.K. Er, M. So. "Thermal annealing behavior of Si-doped diamond like-carbon films deposited by reactive sputtering". J. Ceram. Process. Res. 2010 11 (6) 760–764.C.F.M. Borges, E. Pfender, et al. "Influence of nitrided and carbonitrided interlayers on enhanced nucleation of diamond on stainless steel 304", Diam. Relat. Mater. 2001 10 (11) 1983–1990V.J. Trava-Airoldi, L.F. Bonetti, et al. "DLC film properties obtained by a low cost and modified pulsed-DC discharge". Thin Solid Films 2007 516 (2-4) 272–276.J. Choi, K. Soejima, et al. "Nitriding of high speed steel by bipolar PBII for improvement in adhesion strength of DLC films". Nucl. Instrum. Meth B 2012 272 357–360.C. Casiraghi, A.C. Ferrari, et al. "Raman spectroscopy of hydrogenated amorphous carbons", Phys. Rev. B. 2005 72 1–13.info:eu-repo/semantics/openAccess2016-06-16T21:52:47Zhttp://creativecommons.org/licenses/by-nc-nd/3.0/us/Dalibón Bähler, Eugenia Laura ; Ghafoor, Naureen ; Rogström, Lina ; Trava-Airoldi, Vladimir Jesús ; Odén Magnus ; Brühl, Sonia PatriciaNo comercial con fines académicos.Attribution-NonCommercial-NoDerivs 3.0 United Statesreponame:Repositorio Institucional Abierto (UTN)instname:Universidad Tecnológica Nacional2026-09-24T12:46:15Zoai:ria.utn.edu.ar:20.500.12272/815instacron:UTNInstitucionalhttp://ria.utn.edu.ar/Universidad públicaNo correspondehttp://ria.utn.edu.ar/oaigestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:a2026-09-24 12:46:16.093Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacionalfalse
dc.title.none.fl_str_mv Thermal stability of DLC coating deposited on precipitation hardening stainless steels
Topic : 21. Thin films and surface treatments thermal stability of DLC coating deposited on precipitation hardening stainless steels
title Thermal stability of DLC coating deposited on precipitation hardening stainless steels
spellingShingle Thermal stability of DLC coating deposited on precipitation hardening stainless steels
Dalibón Bähler, Eugenia Laura
DLC coating
Duplex treatment
Thermal stability
Stainless steel
Recubrimientos DLC
Tratamientos duplex
Estabilidad térmica
Aceros inoxidables
title_short Thermal stability of DLC coating deposited on precipitation hardening stainless steels
title_full Thermal stability of DLC coating deposited on precipitation hardening stainless steels
title_fullStr Thermal stability of DLC coating deposited on precipitation hardening stainless steels
title_full_unstemmed Thermal stability of DLC coating deposited on precipitation hardening stainless steels
title_sort Thermal stability of DLC coating deposited on precipitation hardening stainless steels
dc.creator.none.fl_str_mv Dalibón Bähler, Eugenia Laura
Ghafoor, Naureen
Rogström, Lina
Trava-Airoldi, Vladimir Jesús
Odén, Magnus
Brühl, Sonia Patricia
author Dalibón Bähler, Eugenia Laura
author_facet Dalibón Bähler, Eugenia Laura
Ghafoor, Naureen
Rogström, Lina
Trava-Airoldi, Vladimir Jesús
Odén, Magnus
Brühl, Sonia Patricia
author_role author
author2 Ghafoor, Naureen
Rogström, Lina
Trava-Airoldi, Vladimir Jesús
Odén, Magnus
Brühl, Sonia Patricia
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv DLC coating
Duplex treatment
Thermal stability
Stainless steel
Recubrimientos DLC
Tratamientos duplex
Estabilidad térmica
Aceros inoxidables
topic DLC coating
Duplex treatment
Thermal stability
Stainless steel
Recubrimientos DLC
Tratamientos duplex
Estabilidad térmica
Aceros inoxidables
dc.description.none.fl_txt_mv Relationship between nanohardness and annealing temperature of DLC coating on duplex (previously nitrided) and only coated PH steel samples.
The DLC (Diamond Like Carbon) coatings are characterized by good mechanical properties, low friction coefficient and chemical inertness. However, these coatings have problems at high temperature (400 °C) owing to the graphitization which leads to an increase in sp2 and decrease in sp3 bonding structure. In this work, the thermal stability of DLC coatings deposited by PACVD (Plasma-assisted chemical vapor deposition) on nitrided precipitation hardening stainless steel (duplex sample) and without nitriding (coated sample) was studied. The annealing treatments were carried out at 200 °C , 300 °C, 400 °C , 500 °C , 600 °C, 700 °C for 1 hour on coated and duplex samples in vacuum, according to some reports found in the literature. The coatings were characterized by EDS and Raman and hardness was assessed with nanoindentation. The microstructure of the nitrided layer and the coatings was analyzed by OM and SEM. The coatings had about 12 % hydrogen content and the film thickness was about 3 m. The mean hardness of the duplex sample was 16 GPa without annealing, but it did not decrease and remained approximately constant until 600 °C. However, in the coated sample, the hardness decreased at 300 °C, probably because the sp2 bonds percentage increased in the coating. Moreover, at 600 °C, it was not possible to obtain a value for the nanohardness because the dispersion resulted very large. This could be due to coating detachment in several regions, probably caused by film transformation (graphitization) in these zones. It is possible that in the duplex sample, the nitriding process as previous treatment to the coating deposition improved the thermal behavior of the system. Future analysis will be performed in order to identify the compounds that were formed in the interface of the duplex sample.
Los recubrimientos DLC (Diamond Like Carbon) se caracterizan por sus buenas propiedades mecánicas, bajo coeficiente de fricción e inercia química. Sin embargo, estos recubrimientos tienen problemas a alta temperatura (400 °C) debido a que se produce la grafitización que conduce a un aumento de uniones sp2 y a una disminución de las uniones sp3. En este trabajo, se estudió la estabilidad térmica de los recubrimientos DLC depositados por PACVD (Plasma-assisted chemical vapor deposition) sobre acero inoxidable endurecible por precipitación nitrurado (muestra duplex) y sin nitrurar (muestra recubierta). Los tratamientos de recocidos se llevaron a cabo a 200 °C, 300 °C, 400 °C, 500 °C, 600 °C y 700 °C durante una hora en vacío en la muestra duplex y recubierta, de acuerdo a lo reportado en la literatura. Los recubrimientos fueron caracterizados por EDS y Raman y la dureza fue medida con nanoindentación. La microestructura de la capa nitrurada y del recubrimiento fue analizada por OM y SEM. El recubrimiento tuvo un contenido de hidrógeno de aproximadamente el 12 % y su espesor fue de aproximadamente 3 m. El valor de dureza promedio en la muestra duplex fue de 16 GPa antes del recocido y permaneció aproximadamente constante hasta 600 °C. Sin embargo, en la muestra recubierta, la dureza disminuyó a los 300 °C probablemente porque el porcentaje de uniones sp2 aumentó en el recubrimiento. Además a 600 °C no fue posible obtener un valor para la nanodureza porque hubo una gran dispersión en los valores. Esto podría deberse a que el recubrimiento se desprendió en algunas regiones probablemente a causa de su grafitización en esas zonas. Es posible que en la muestra duplex, el proceso de nitruración previo al tratamiento de deposición del recubrimiento mejoró el comportamiento térmico del sistema. En el futuro, se realizarán análisis para identificar los compuestos que se forman en la interfase de la muestra duplex.
Fil: Dalibón Bähler, Eugenia Laura. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.
Fil: Ghafoor, Naureen. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.
Fil: Rogström, Lina. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.
Fil: Trava-Airoldi, Vladimir Jesús. Instituto Nacional de Pesquisas Espaciáis; Brazil.
Fil: Odén, Magnus. Linköping University. Nanostructured Materials, Department of Physics, Chemistry and Biology; Sweden.
Fil: Brühl, Sonia Patricia. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.
Peer Reviewed
description Relationship between nanohardness and annealing temperature of DLC coating on duplex (previously nitrided) and only coated PH steel samples.
publishDate 2015
dc.date.none.fl_str_mv 2015-11-17
2016-06-16T21:52:47Z
2016-06-16T21:52:47Z
dc.type.none.fl_str_mv info:eu-repo/semantics/conferenceObject
info:eu-repo/semantics/acceptedVersion
docunento de conferencia
http://purl.org/coar/resource_type/c_5794
info:ar-repo/semantics/documentoDeConferencia
format conferenceObject
status_str acceptedVersion
dc.identifier.none.fl_str_mv 15º Congreso Internacional de Metalurgia y Materiales CONAMET/SAM. Chile (2015)
http://hdl.handle.net/20.500.12272/815
identifier_str_mv 15º Congreso Internacional de Metalurgia y Materiales CONAMET/SAM. Chile (2015)
url http://hdl.handle.net/20.500.12272/815
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv H. Li, T. Xu, et al. "Annealing effect on the structure, mechanical and tribological properties of hydrogenated diamond-like carbon films" Thin Solid Films 2006 515 (4) 2153–2160
Y.S. Zou, Y.F. Wu, et al. "Mechanical properties and thermal stability of nitrogen incorporated diamond-like carbon films", Vacuum 2009 83 (11) 1406–1410.
Zhang, X.L. Bui, et al, "Thermal stability and oxidation properties of magnetron sputtered diamond-like carbon and its nanocomposite coatings". Diam. Relat. Mater. 2006 15 (4-8) 972–976.
H.W. Choi, D.M. Gage, et al. "Effects of thermal annealing and Si incorporation on bonding structure and fracture properties of diamond-like carbon films". Diam. Relat. Mater. 2009 18 (4) 615–619.
K. Er, M. So. "Thermal annealing behavior of Si-doped diamond like-carbon films deposited by reactive sputtering". J. Ceram. Process. Res. 2010 11 (6) 760–764.
C.F.M. Borges, E. Pfender, et al. "Influence of nitrided and carbonitrided interlayers on enhanced nucleation of diamond on stainless steel 304", Diam. Relat. Mater. 2001 10 (11) 1983–1990
V.J. Trava-Airoldi, L.F. Bonetti, et al. "DLC film properties obtained by a low cost and modified pulsed-DC discharge". Thin Solid Films 2007 516 (2-4) 272–276.
J. Choi, K. Soejima, et al. "Nitriding of high speed steel by bipolar PBII for improvement in adhesion strength of DLC films". Nucl. Instrum. Meth B 2012 272 357–360.
C. Casiraghi, A.C. Ferrari, et al. "Raman spectroscopy of hydrogenated amorphous carbons", Phys. Rev. B. 2005 72 1–13.
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
2016-06-16T21:52:47Z
http://creativecommons.org/licenses/by-nc-nd/3.0/us/
Dalibón Bähler, Eugenia Laura ; Ghafoor, Naureen ; Rogström, Lina ; Trava-Airoldi, Vladimir Jesús ; Odén Magnus ; Brühl, Sonia Patricia
No comercial con fines académicos.
Attribution-NonCommercial-NoDerivs 3.0 United States
eu_rights_str_mv openAccess
rights_invalid_str_mv 2016-06-16T21:52:47Z
http://creativecommons.org/licenses/by-nc-nd/3.0/us/
Dalibón Bähler, Eugenia Laura ; Ghafoor, Naureen ; Rogström, Lina ; Trava-Airoldi, Vladimir Jesús ; Odén Magnus ; Brühl, Sonia Patricia
No comercial con fines académicos.
Attribution-NonCommercial-NoDerivs 3.0 United States
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.source.none.fl_str_mv reponame:Repositorio Institucional Abierto (UTN)
instname:Universidad Tecnológica Nacional
reponame_str Repositorio Institucional Abierto (UTN)
collection Repositorio Institucional Abierto (UTN)
instname_str Universidad Tecnológica Nacional
repository.name.fl_str_mv Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacional
repository.mail.fl_str_mv gestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.ar
_version_ 1877230917990219776
score 13.265058

Publicaciones similares