Estructuras de titanio porosas. Fabricación y caracterización.

Autores
López Padilla, Roger; Oldani, Carlos; Grinschpun , Luciano; Lucci, Roberto; Roure, César
Año de publicación
2015
Idioma
español castellano
Tipo de recurso
artículo
Estado
versión aceptada
Descripción
It was studied the space particles process to obtain porous titanium structures, that consist in mixing the powders to be sintered with a component that volatilizes at low temperatures. In this case it was used the acid ammonium carbonate, which leaves gaps (pores) in the structure as it sublimates. There were obtained titanium compacts with open porosity between 35 % and 72 % and pore size between 200 mm and 300 mm. Moreover, there were performed initial studies to obtain titanium compacts with porosity gradient using sequential compaction, to obtain differentiated values of the elasticity modulus between the surface and the center, comparable to those observed in bone. The porous compacts obtained were characterized by optical and electron microscopy to evaluate the microstructure, and compression tests were performed to determine the values of yield strength and elastic modulus. The influence of the main process parameters were determined; percentage and size of the spacer particles, compaction pressure, sintering temperature and time, the values of elasticity modulus, yield strength and microstructure. The results indicates that it is possible to adjust the values of elastic modulus and yield strength of porous titanium compacts produced, so that resemble those with both trabecular and cortical bone. Additionally, it can be adjust the porosity achieved, to the values given in the literature as such as those that meet the needs of vascularization and transport of metabolic products that are critical in the formation of bone tissue. The pore size range reached is within the recommended values for a correct integration of the porous material in the bone, allowing good cell adhesion and migration.
Para la obtención de estructuras de titanio porosas se estudió el proceso de partículas espaciadoras, que consiste en mezclar los polvos a sinterizar con un componente que volatiliza a bajas temperaturas, en este caso el carbonato ácido de amonio, y que al hacerlo deja espacios vacíos (poros) en la estructura. Se obtuvieron compactos de titanio con porosidad abierta entre 35 % y 72 % y tamaño de poro entre 200 mm y 300 mm. Además, se efectuaron estudios iniciales de fabricación de compactos de titanio con gradiente de porosidad mediante compactación secuencial, a fin de obtener valores de módulo de elasticidad diferenciado entre la superficie y el centro comparables a los que se observan en los huesos. Se caracterizaron los compactos porosos obtenidos mediante microscopía óptica y electrónica para evaluar la microestructura y a través de ensayos de compresión para determinar los valores de límite de fluencia y módulo de elasticidad. Se determinó la influencia de los principales parámetros del proceso; porcentaje y granulometría de las partículas espaciadoras, presión de compactación, temperatura y tiempo de sinterización, sobre los valores de módulo de elasticidad, límite de fluencia y microestructura. Los resultados obtenidos indican que es posible ajustar los valores de módulo de elasticidad y límite de fluencia de los compactos porosos de titanio producidos, de manera que se asemejen a los que poseen tanto los huesos trabeculares como corticales. Además, se pueden adecuar las porosidades alcanzadas, a los valores indicados en la bibliografía, como aquellos que satisfacen las necesidades de vascularización y transporte de productos metabólicos que son fundamentales en la formación del tejido óseo. El rango de tamaño de poro alcanzado se encuentra dentro de los valores recomendados, para una correcta integración del material poroso con el hueso alojante ya que permiten una buena migración y adhesión celular.
Fil: López Padilla, Roger. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Oldani, Carlos. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Grinschpun, Luciano. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Lucci, Roberto. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Roure, César. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Materia
Titanio
Estructuras porosas
Sinterización
Pulvimetalurgia
Nivel de accesibilidad
acceso abierto
Condiciones de uso
Attribution-NonCommercial-NoDerivatives 4.0 International
Repositorio
Repositorio Institucional Abierto (UTN)
Institución
Universidad Tecnológica Nacional
OAI Identificador
oai:ria.utn.edu.ar:20.500.12272/13453
Acceder
id RIAUTN_d6267260976488deb8862c0ab50ac8ac
oai_identifier_str oai:ria.utn.edu.ar:20.500.12272/13453
network_acronym_str RIAUTN
repository_id_str a
network_name_str Repositorio Institucional Abierto (UTN)
spelling Estructuras de titanio porosas. Fabricación y caracterización.López Padilla, RogerOldani, CarlosGrinschpun , LucianoLucci, RobertoRoure, CésarTitanioEstructuras porosasSinterizaciónPulvimetalurgiaIt was studied the space particles process to obtain porous titanium structures, that consist in mixing the powders to be sintered with a component that volatilizes at low temperatures. In this case it was used the acid ammonium carbonate, which leaves gaps (pores) in the structure as it sublimates. There were obtained titanium compacts with open porosity between 35 % and 72 % and pore size between 200 mm and 300 mm. Moreover, there were performed initial studies to obtain titanium compacts with porosity gradient using sequential compaction, to obtain differentiated values of the elasticity modulus between the surface and the center, comparable to those observed in bone. The porous compacts obtained were characterized by optical and electron microscopy to evaluate the microstructure, and compression tests were performed to determine the values of yield strength and elastic modulus. The influence of the main process parameters were determined; percentage and size of the spacer particles, compaction pressure, sintering temperature and time, the values of elasticity modulus, yield strength and microstructure. The results indicates that it is possible to adjust the values of elastic modulus and yield strength of porous titanium compacts produced, so that resemble those with both trabecular and cortical bone. Additionally, it can be adjust the porosity achieved, to the values given in the literature as such as those that meet the needs of vascularization and transport of metabolic products that are critical in the formation of bone tissue. The pore size range reached is within the recommended values for a correct integration of the porous material in the bone, allowing good cell adhesion and migration.Para la obtención de estructuras de titanio porosas se estudió el proceso de partículas espaciadoras, que consiste en mezclar los polvos a sinterizar con un componente que volatiliza a bajas temperaturas, en este caso el carbonato ácido de amonio, y que al hacerlo deja espacios vacíos (poros) en la estructura. Se obtuvieron compactos de titanio con porosidad abierta entre 35 % y 72 % y tamaño de poro entre 200 mm y 300 mm. Además, se efectuaron estudios iniciales de fabricación de compactos de titanio con gradiente de porosidad mediante compactación secuencial, a fin de obtener valores de módulo de elasticidad diferenciado entre la superficie y el centro comparables a los que se observan en los huesos. Se caracterizaron los compactos porosos obtenidos mediante microscopía óptica y electrónica para evaluar la microestructura y a través de ensayos de compresión para determinar los valores de límite de fluencia y módulo de elasticidad. Se determinó la influencia de los principales parámetros del proceso; porcentaje y granulometría de las partículas espaciadoras, presión de compactación, temperatura y tiempo de sinterización, sobre los valores de módulo de elasticidad, límite de fluencia y microestructura. Los resultados obtenidos indican que es posible ajustar los valores de módulo de elasticidad y límite de fluencia de los compactos porosos de titanio producidos, de manera que se asemejen a los que poseen tanto los huesos trabeculares como corticales. Además, se pueden adecuar las porosidades alcanzadas, a los valores indicados en la bibliografía, como aquellos que satisfacen las necesidades de vascularización y transporte de productos metabólicos que son fundamentales en la formación del tejido óseo. El rango de tamaño de poro alcanzado se encuentra dentro de los valores recomendados, para una correcta integración del material poroso con el hueso alojante ya que permiten una buena migración y adhesión celular.Fil: López Padilla, Roger. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.Fil: Oldani, Carlos. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.Fil: Grinschpun, Luciano. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.Fil: Lucci, Roberto. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.Fil: Roure, César. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.Conamet/Sam.2025-07-03T19:46:42Z2015info:eu-repo/semantics/articleinfo:eu-repo/semantics/acceptedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articulopdfapplication/pdfConamet/Sam 2015.https://hdl.handle.net/20.500.12272/13453spainfo:eu-repo/semantics/openAccessAttribution-NonCommercial-NoDerivatives 4.0 Internationalhttp://creativecommons.org/licenses/by-nc-nd/4.0/López Padilla, Roger; Oldani, Carlos; Grinschpun, Luciano; Lucci, Roberto; Roure, César.https://creativecommons.org/licenses/by-nc-nd/4.0/reponame:Repositorio Institucional Abierto (UTN)instname:Universidad Tecnológica Nacional2026-09-24T12:45:46Zoai:ria.utn.edu.ar:20.500.12272/13453instacron:UTNInstitucionalhttp://ria.utn.edu.ar/Universidad públicaNo correspondehttp://ria.utn.edu.ar/oaigestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:a2026-09-24 12:45:48.076Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacionalfalse
dc.title.none.fl_str_mv Estructuras de titanio porosas. Fabricación y caracterización.
title Estructuras de titanio porosas. Fabricación y caracterización.
spellingShingle Estructuras de titanio porosas. Fabricación y caracterización.
López Padilla, Roger
Titanio
Estructuras porosas
Sinterización
Pulvimetalurgia
title_short Estructuras de titanio porosas. Fabricación y caracterización.
title_full Estructuras de titanio porosas. Fabricación y caracterización.
title_fullStr Estructuras de titanio porosas. Fabricación y caracterización.
title_full_unstemmed Estructuras de titanio porosas. Fabricación y caracterización.
title_sort Estructuras de titanio porosas. Fabricación y caracterización.
dc.creator.none.fl_str_mv López Padilla, Roger
Oldani, Carlos
Grinschpun , Luciano
Lucci, Roberto
Roure, César
author López Padilla, Roger
author_facet López Padilla, Roger
Oldani, Carlos
Grinschpun , Luciano
Lucci, Roberto
Roure, César
author_role author
author2 Oldani, Carlos
Grinschpun , Luciano
Lucci, Roberto
Roure, César
author2_role author
author
author
author
dc.subject.none.fl_str_mv Titanio
Estructuras porosas
Sinterización
Pulvimetalurgia
topic Titanio
Estructuras porosas
Sinterización
Pulvimetalurgia
dc.description.none.fl_txt_mv It was studied the space particles process to obtain porous titanium structures, that consist in mixing the powders to be sintered with a component that volatilizes at low temperatures. In this case it was used the acid ammonium carbonate, which leaves gaps (pores) in the structure as it sublimates. There were obtained titanium compacts with open porosity between 35 % and 72 % and pore size between 200 mm and 300 mm. Moreover, there were performed initial studies to obtain titanium compacts with porosity gradient using sequential compaction, to obtain differentiated values of the elasticity modulus between the surface and the center, comparable to those observed in bone. The porous compacts obtained were characterized by optical and electron microscopy to evaluate the microstructure, and compression tests were performed to determine the values of yield strength and elastic modulus. The influence of the main process parameters were determined; percentage and size of the spacer particles, compaction pressure, sintering temperature and time, the values of elasticity modulus, yield strength and microstructure. The results indicates that it is possible to adjust the values of elastic modulus and yield strength of porous titanium compacts produced, so that resemble those with both trabecular and cortical bone. Additionally, it can be adjust the porosity achieved, to the values given in the literature as such as those that meet the needs of vascularization and transport of metabolic products that are critical in the formation of bone tissue. The pore size range reached is within the recommended values for a correct integration of the porous material in the bone, allowing good cell adhesion and migration.
Para la obtención de estructuras de titanio porosas se estudió el proceso de partículas espaciadoras, que consiste en mezclar los polvos a sinterizar con un componente que volatiliza a bajas temperaturas, en este caso el carbonato ácido de amonio, y que al hacerlo deja espacios vacíos (poros) en la estructura. Se obtuvieron compactos de titanio con porosidad abierta entre 35 % y 72 % y tamaño de poro entre 200 mm y 300 mm. Además, se efectuaron estudios iniciales de fabricación de compactos de titanio con gradiente de porosidad mediante compactación secuencial, a fin de obtener valores de módulo de elasticidad diferenciado entre la superficie y el centro comparables a los que se observan en los huesos. Se caracterizaron los compactos porosos obtenidos mediante microscopía óptica y electrónica para evaluar la microestructura y a través de ensayos de compresión para determinar los valores de límite de fluencia y módulo de elasticidad. Se determinó la influencia de los principales parámetros del proceso; porcentaje y granulometría de las partículas espaciadoras, presión de compactación, temperatura y tiempo de sinterización, sobre los valores de módulo de elasticidad, límite de fluencia y microestructura. Los resultados obtenidos indican que es posible ajustar los valores de módulo de elasticidad y límite de fluencia de los compactos porosos de titanio producidos, de manera que se asemejen a los que poseen tanto los huesos trabeculares como corticales. Además, se pueden adecuar las porosidades alcanzadas, a los valores indicados en la bibliografía, como aquellos que satisfacen las necesidades de vascularización y transporte de productos metabólicos que son fundamentales en la formación del tejido óseo. El rango de tamaño de poro alcanzado se encuentra dentro de los valores recomendados, para una correcta integración del material poroso con el hueso alojante ya que permiten una buena migración y adhesión celular.
Fil: López Padilla, Roger. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Oldani, Carlos. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Grinschpun, Luciano. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Lucci, Roberto. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
Fil: Roure, César. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Departamento Ingeniería Metalúrgica; Argentina.
description It was studied the space particles process to obtain porous titanium structures, that consist in mixing the powders to be sintered with a component that volatilizes at low temperatures. In this case it was used the acid ammonium carbonate, which leaves gaps (pores) in the structure as it sublimates. There were obtained titanium compacts with open porosity between 35 % and 72 % and pore size between 200 mm and 300 mm. Moreover, there were performed initial studies to obtain titanium compacts with porosity gradient using sequential compaction, to obtain differentiated values of the elasticity modulus between the surface and the center, comparable to those observed in bone. The porous compacts obtained were characterized by optical and electron microscopy to evaluate the microstructure, and compression tests were performed to determine the values of yield strength and elastic modulus. The influence of the main process parameters were determined; percentage and size of the spacer particles, compaction pressure, sintering temperature and time, the values of elasticity modulus, yield strength and microstructure. The results indicates that it is possible to adjust the values of elastic modulus and yield strength of porous titanium compacts produced, so that resemble those with both trabecular and cortical bone. Additionally, it can be adjust the porosity achieved, to the values given in the literature as such as those that meet the needs of vascularization and transport of metabolic products that are critical in the formation of bone tissue. The pore size range reached is within the recommended values for a correct integration of the porous material in the bone, allowing good cell adhesion and migration.
publishDate 2015
dc.date.none.fl_str_mv 2015
2025-07-03T19:46:42Z
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/acceptedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str acceptedVersion
dc.identifier.none.fl_str_mv Conamet/Sam 2015.
https://hdl.handle.net/20.500.12272/13453
identifier_str_mv Conamet/Sam 2015.
url https://hdl.handle.net/20.500.12272/13453
dc.language.none.fl_str_mv spa
language spa
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
Attribution-NonCommercial-NoDerivatives 4.0 International
http://creativecommons.org/licenses/by-nc-nd/4.0/
López Padilla, Roger; Oldani, Carlos; Grinschpun, Luciano; Lucci, Roberto; Roure, César.
https://creativecommons.org/licenses/by-nc-nd/4.0/
eu_rights_str_mv openAccess
rights_invalid_str_mv Attribution-NonCommercial-NoDerivatives 4.0 International
http://creativecommons.org/licenses/by-nc-nd/4.0/
López Padilla, Roger; Oldani, Carlos; Grinschpun, Luciano; Lucci, Roberto; Roure, César.
https://creativecommons.org/licenses/by-nc-nd/4.0/
dc.format.none.fl_str_mv pdf
application/pdf
dc.publisher.none.fl_str_mv Conamet/Sam.
publisher.none.fl_str_mv Conamet/Sam.
dc.source.none.fl_str_mv reponame:Repositorio Institucional Abierto (UTN)
instname:Universidad Tecnológica Nacional
reponame_str Repositorio Institucional Abierto (UTN)
collection Repositorio Institucional Abierto (UTN)
instname_str Universidad Tecnológica Nacional
repository.name.fl_str_mv Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacional
repository.mail.fl_str_mv gestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.ar
_version_ 1877230909434888192
score 13.24418

Publicaciones similares