Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites

Autores
Gómez Costa, Marcos Bruno; Juárez, Juliana; Martínez, María Laura; Beltramone, Andrea Raquel; Cussa, Jorgelina; Anunziata, Oscar Alfredo
Año de publicación
2012
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Si-SBA-3 and Na–AlSBA-3 materials were synthesized for application in the preparation of composites. Silica mesoporous materials were obtained following the sol–gel method and post-synthesis alumination. Pyrrole-saturated hosts were prepared by adsorption of pyrrole into the mesoporous materials. The adsorption/desorption of pyrrole was studied by FTIR. Molecules of pyrrole would be adsorbed through aromatic ring to the host. The polymerization technique was performed by oxidative way using different oxidizing agents, ammonium persulfate and ferric chloride, after pyrrole adsorption on both hosts. TG, FTIR, BET, XRD, SEM and TEM were used to characterize the resulting composites. These studies show that polypyrrole is generated inside the channel of the hosts; conductivity studies show that the composites exhibit conductivities at room temperature and in the range of 1 × 10—7 and 1 × 10—6 S cm—1 depending on the host and the oxidizing agents.
Fil: Gómez Costa, Marcos Bruno. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Fil: Juárez, Juliana. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina
Fil: Martínez, María Laura. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina
Fil: Beltramone, Andrea Raquel. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Fil: Cussa, Jorgelina. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Fil: Anunziata, Oscar Alfredo. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Peer Reviewed
Materia
composites
nanostructures
Polymers
infrared
infrared spectroscopy
X-ray diffraction
Nivel de accesibilidad
acceso abierto
Condiciones de uso
2024-04-04T20:28:11Z
Repositorio
Repositorio Institucional Abierto (UTN)
Institución
Universidad Tecnológica Nacional
OAI Identificador
oai:ria.utn.edu.ar:20.500.12272/10327
Acceder
id RIAUTN_da31dadc17d5b257cf80aa885270ca18
oai_identifier_str oai:ria.utn.edu.ar:20.500.12272/10327
network_acronym_str RIAUTN
repository_id_str a
network_name_str Repositorio Institucional Abierto (UTN)
spelling Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 compositesGómez Costa, Marcos BrunoJuárez, JulianaMartínez, María LauraBeltramone, Andrea RaquelCussa, JorgelinaAnunziata, Oscar AlfredocompositesnanostructuresPolymersinfraredinfrared spectroscopyX-ray diffractionSi-SBA-3 and Na–AlSBA-3 materials were synthesized for application in the preparation of composites. Silica mesoporous materials were obtained following the sol–gel method and post-synthesis alumination. Pyrrole-saturated hosts were prepared by adsorption of pyrrole into the mesoporous materials. The adsorption/desorption of pyrrole was studied by FTIR. Molecules of pyrrole would be adsorbed through aromatic ring to the host. The polymerization technique was performed by oxidative way using different oxidizing agents, ammonium persulfate and ferric chloride, after pyrrole adsorption on both hosts. TG, FTIR, BET, XRD, SEM and TEM were used to characterize the resulting composites. These studies show that polypyrrole is generated inside the channel of the hosts; conductivity studies show that the composites exhibit conductivities at room temperature and in the range of 1 × 10—7 and 1 × 10—6 S cm—1 depending on the host and the oxidizing agents.Fil: Gómez Costa, Marcos Bruno. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.Fil: Juárez, Juliana. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; ArgentinaFil: Martínez, María Laura. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; ArgentinaFil: Beltramone, Andrea Raquel. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.Fil: Cussa, Jorgelina. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.Fil: Anunziata, Oscar Alfredo. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.Peer Reviewed2024-04-04T20:28:11Z2024-04-04T20:28:11Z2012info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articulopdfapplication/pdfhttp://hdl.handle.net/20.500.12272/10327-enginfo:eu-repo/semantics/openAccess2024-04-04T20:28:11Zhttp://creativecommons.org/licenses/by-nc-nd/4.0/Attribution-NonCommercial-NoDerivatives 4.0 InternacionalBeltramone, Andrea Raquel_X_Atribución (Attribution): En cualquier explotación de la obra autorizada por la licencia será necesario reconocer la autoría (obligatoria en todos los casos). _X_No comercial (Non Commercial): La explotación de la obra queda limitada a usos no comerciales. _X_Sin obras derivadas (No Derivate Works): La autorización para explotar la obra no incluye la posibilidad de crear una obra derivada (traducciones, adaptaciones, etc.). _X_Compartir igual (Share Alike): La explotación autorizada incluye la creación de obras derivadas siempre que se mantenga la misma licencia al ser divulgadas.reponame:Repositorio Institucional Abierto (UTN)instname:Universidad Tecnológica Nacional2026-09-24T12:48:13Zoai:ria.utn.edu.ar:20.500.12272/10327instacron:UTNInstitucionalhttp://ria.utn.edu.ar/Universidad públicaNo correspondehttp://ria.utn.edu.ar/oaigestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:a2026-09-24 12:48:14.014Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacionalfalse
dc.title.none.fl_str_mv Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
title Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
spellingShingle Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
Gómez Costa, Marcos Bruno
composites
nanostructures
Polymers
infrared
infrared spectroscopy
X-ray diffraction
title_short Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
title_full Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
title_fullStr Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
title_full_unstemmed Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
title_sort Synthesis and characterization of conducting polypyrrole/SBA-3 and polypyrrole/Na–AlSBA-3 composites
dc.creator.none.fl_str_mv Gómez Costa, Marcos Bruno
Juárez, Juliana
Martínez, María Laura
Beltramone, Andrea Raquel
Cussa, Jorgelina
Anunziata, Oscar Alfredo
author Gómez Costa, Marcos Bruno
author_facet Gómez Costa, Marcos Bruno
Juárez, Juliana
Martínez, María Laura
Beltramone, Andrea Raquel
Cussa, Jorgelina
Anunziata, Oscar Alfredo
author_role author
author2 Juárez, Juliana
Martínez, María Laura
Beltramone, Andrea Raquel
Cussa, Jorgelina
Anunziata, Oscar Alfredo
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv composites
nanostructures
Polymers
infrared
infrared spectroscopy
X-ray diffraction
topic composites
nanostructures
Polymers
infrared
infrared spectroscopy
X-ray diffraction
dc.description.none.fl_txt_mv Si-SBA-3 and Na–AlSBA-3 materials were synthesized for application in the preparation of composites. Silica mesoporous materials were obtained following the sol–gel method and post-synthesis alumination. Pyrrole-saturated hosts were prepared by adsorption of pyrrole into the mesoporous materials. The adsorption/desorption of pyrrole was studied by FTIR. Molecules of pyrrole would be adsorbed through aromatic ring to the host. The polymerization technique was performed by oxidative way using different oxidizing agents, ammonium persulfate and ferric chloride, after pyrrole adsorption on both hosts. TG, FTIR, BET, XRD, SEM and TEM were used to characterize the resulting composites. These studies show that polypyrrole is generated inside the channel of the hosts; conductivity studies show that the composites exhibit conductivities at room temperature and in the range of 1 × 10—7 and 1 × 10—6 S cm—1 depending on the host and the oxidizing agents.
Fil: Gómez Costa, Marcos Bruno. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Fil: Juárez, Juliana. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina
Fil: Martínez, María Laura. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina
Fil: Beltramone, Andrea Raquel. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Fil: Cussa, Jorgelina. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Fil: Anunziata, Oscar Alfredo. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología. Córdoba; Argentina.
Peer Reviewed
description Si-SBA-3 and Na–AlSBA-3 materials were synthesized for application in the preparation of composites. Silica mesoporous materials were obtained following the sol–gel method and post-synthesis alumination. Pyrrole-saturated hosts were prepared by adsorption of pyrrole into the mesoporous materials. The adsorption/desorption of pyrrole was studied by FTIR. Molecules of pyrrole would be adsorbed through aromatic ring to the host. The polymerization technique was performed by oxidative way using different oxidizing agents, ammonium persulfate and ferric chloride, after pyrrole adsorption on both hosts. TG, FTIR, BET, XRD, SEM and TEM were used to characterize the resulting composites. These studies show that polypyrrole is generated inside the channel of the hosts; conductivity studies show that the composites exhibit conductivities at room temperature and in the range of 1 × 10—7 and 1 × 10—6 S cm—1 depending on the host and the oxidizing agents.
publishDate 2012
dc.date.none.fl_str_mv 2012
2024-04-04T20:28:11Z
2024-04-04T20:28:11Z
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/20.500.12272/10327
-
url http://hdl.handle.net/20.500.12272/10327
identifier_str_mv -
dc.language.none.fl_str_mv eng
language eng
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
2024-04-04T20:28:11Z
http://creativecommons.org/licenses/by-nc-nd/4.0/
Attribution-NonCommercial-NoDerivatives 4.0 Internacional
Beltramone, Andrea Raquel
_X_Atribución (Attribution): En cualquier explotación de la obra autorizada por la licencia será necesario reconocer la autoría (obligatoria en todos los casos). _X_No comercial (Non Commercial): La explotación de la obra queda limitada a usos no comerciales. _X_Sin obras derivadas (No Derivate Works): La autorización para explotar la obra no incluye la posibilidad de crear una obra derivada (traducciones, adaptaciones, etc.). _X_Compartir igual (Share Alike): La explotación autorizada incluye la creación de obras derivadas siempre que se mantenga la misma licencia al ser divulgadas.
eu_rights_str_mv openAccess
rights_invalid_str_mv 2024-04-04T20:28:11Z
http://creativecommons.org/licenses/by-nc-nd/4.0/
Attribution-NonCommercial-NoDerivatives 4.0 Internacional
Beltramone, Andrea Raquel
_X_Atribución (Attribution): En cualquier explotación de la obra autorizada por la licencia será necesario reconocer la autoría (obligatoria en todos los casos). _X_No comercial (Non Commercial): La explotación de la obra queda limitada a usos no comerciales. _X_Sin obras derivadas (No Derivate Works): La autorización para explotar la obra no incluye la posibilidad de crear una obra derivada (traducciones, adaptaciones, etc.). _X_Compartir igual (Share Alike): La explotación autorizada incluye la creación de obras derivadas siempre que se mantenga la misma licencia al ser divulgadas.
dc.format.none.fl_str_mv pdf
application/pdf
dc.source.none.fl_str_mv reponame:Repositorio Institucional Abierto (UTN)
instname:Universidad Tecnológica Nacional
reponame_str Repositorio Institucional Abierto (UTN)
collection Repositorio Institucional Abierto (UTN)
instname_str Universidad Tecnológica Nacional
repository.name.fl_str_mv Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacional
repository.mail.fl_str_mv gestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.ar
_version_ 1877230954805723136
score 13.265058

Publicaciones similares